AFM Scans of Coated, Annealed TEM Windows

This paper parallels my efforts in creating a microfluidic device that can perform co-culturing of different cell types, allow real time phase and fluorescence imaging, and perform non-invasive TEER measurement using transparent electrodes. This is almost exactly what we aimed for; the only difference is in the type of the membrane. They are using a…

Wafer 1148 was produced roughly around the same time that the wafer I used to make my oldest MgF2 material (wafer 1085) was produced. We know that some of the NPN material from that time was not etched all the way through, creating pores that look like a ‘bowl-with-hole’. I believe the shape of the…

Having finished the hydraulic permeability testing with DI water I wanted to see what the effect of an introduction of protein would have on the permeability values. To do this I simply reran a set of fresh membranes at 21.63psi using a 1mg/mL solution of bovine albumin in PBS instead of water.The group on the…

This post is a continuation of the work in Partial Etch RIE Blows out NPN Pores and MgF2 Nanomembrane Fabrication on partially etched NPN substrates. We believe the underlying NPN template influences the shape of our SERS active nanostructures and therefore the SERS properties. In this post, we’ll take a look at some of the structures resulting…

Last week Dave deposited sep-cons ( cell culture mask) with 3 different thickness namely the regular 15nm , 30 nm and 50nm ( SC 142, 143,144). These wafers were characterized and it was noted that the 15 nm had a high pinhole density and the 30 and 50 nm films were low pinhole density.  The…

These are the sieving curves for 50, 75, and 100 nm NPN membranes. The 75 nm NPN 30 nm gold data point is just an estimate, since the membrane broke before enough filtrate could be collected for an absorbance measurement. However, our estimates of zero gold tend to be pretty good (gold is very visible in solution,…