In continuation of the previous post, I ran the pore processing software for two samples (t=0 and t=150 min). The following histograms show the pore parameters and the difference in the pore size and numbers between the two samples. I am not sure if the difference between the pore sizes could be due to sample-sample…
There has been uncertainty with process of dissolution of pnc-Si in cell growth media. Whether the media enters the pores and ‘eats away’ the material leading to increase in pore sizes and eventually complete degradation was the question. Thinning of the material would have taken place too. To have a clear picture about this, I…
After recent studies with surface treatments, we wanted to take a step further by trying amino silanization on RTP’ed samples. Wafer 413 samples were RTP’d with no intact slits. Both 2D and 3D formats were tested in DMEM (-FBS) in oven @37C. All 3D samples had membrane side facing down whereas, in 2D format the…
A bunch of samples from W683 (no RTP) were liquid silanized and used in 3D format to track discoloration in comparison to control sample, in DMEM(-FBS) @ 37C in Oven. I used all the cracked chips which broke while clamping them into Sepcons. Instead of tossing them off, I just wanted to repeat the discoloration…
Surface treatments like silanization were seen to slow down discoloration in the past. I carried out liquid amino-silanization (protocol in place) of samples from W683 (no RTP) and used them in both 2D and 3D format to monitor discoloration in DMEM(-FBS) @ 37C in Oven. Also BSA coated samples were used side by side for…
I carried out a repetition of BSA coating experiment with both 2D and 3D formats. With 2D, I get the same result as before, but surprisingly, in Sepcon 3D format we observe the opposite to what we see in 2D! (can be seen in the figure below) All the three samples with different BSA coatings…
I coated the pncSi samples from W683 (no RTP) with Bovine Serum Albumin (BSA) in Tris-EDTA buffer. Three different concentrations were used: 1 mg/ml, 5 mg/ml and 10 mg/ml (usual range of BSA conc. used for coating Si surfaces). The samples were left in BSA solution for 45-60 mins at room temperature and almost dried,…
Repeated the previous experiment with W683 and following images were captured after 5 hours of incubation in DMEM(-FBS), Oven @ 37C. I took Sepcon samples with regular thin o-rings, fat o-ring, without o-ring and w/grease in place of o-rings. Also for comparison, used cloning rings and the 2D flat format (left=w/o grease, right=w/grease) samples. All…
I carried out this experiment in order to rule out any effect due to geometry of the setup in our discoloration experiments in Sepcon. I used a cloning ring and mimicked the Sepcon as shown in the figure below. The only difference is the o-ring which is absent in the cloning ring setup. To cover…
In an effort to imitate Sepcon, I applied nail polish on two samples covering the edges and the back side (well side) and compared its discoloration to Sepcon format and w/o polish sample in 2D format. I used two polished samples in which I covered the edges in both but the back side was not…